Product Name: ceramic wearing compound
Density: 2.25 g/cm3
Weight Ratio: 3:1
Compressive Strength: 110.0 MPa
Certifified: ISO 9001
Tensile Strength: 28.0 MPa
Working Temperature: -60-120℃

Отправить запрос

Внедрение продукции

Intruduction

Ceramic wearing compound contains hard alumina powder and small ceramic particles as epoxy protective materials as fillers, which has excellent resistance to sliding and friction. It can withstand temperatures up to 120°C and is resistant to a variety of chemical corrosion. It is suitable for resisting the wear of dust and fine particles with a diameter greater than 3mm, such as the wear caused by dust.

Specifications

Series	BM8229
Color	Brown
Density (g/cm3)	2.25
Weight ratio(A:B)	3:1
Volume ratio(A:B)	3:1
Operation time(200g mixing, min)	30
Full curing time(h)	24
After curing hardness(shoreD)	89.0
Compressive strength(MPa)	110.0
Tensile strength(MPa)	28.0
Shear strength(MPa)	16.0
Working temperature(℃)	-60-120
Expiration date(years)	2

Features of Ceramic Alumina Adhesive

Strong bonding ability to various substrate surfaces;
The lining is dense, tough and wear-resistant;
Has good corrosion resistance;
The product is easy to serialize to adapt to different working conditions;
The construction is convenient, and when necessary, quick repairs can be carried out on site.

Applications

Wearing compound can be applied to smooth construction surfaces with a trowel to provide abrasion and corrosion protection for solid material handling or storage equipment surfaces.
Ceramic bead filled epoxy are widely used in fly ash pipe lining, repairing coal ash pumps, mud pumps, water treatment equipment, vertical coal mills, pulverized coal machine conical areas, coal pipelines, ash removal pipelines, primary air ducts, elbows, elbows, etc. Wear parts.